RGBP-ResCom® Global Building Products, founded in Queensland, Australia in 2009. RGBP and our associates have created a strong history of proven performance in the construction industry. Our foundation, built over the past 16 years, is based on lifecycle performance related to outdoor environmental sustainability and healthy, non-toxic indoor product solutions.
ResCom® Boards are an engineered and evolved manufacturing formulation that has registered patents in the United States, Australia, Canada, China, New Zealand, and the United Kingdom, as well as several individual and joint system patents that utilize the ResCom® core material products.
- ResCom® Flat Sheet Fiber Reinforced Magnesia Cement Board has a flame spread index of 10 or less and a smoke-developed index of 5 or less when tested in accordance with ASTM E84. ResCom® Boards are classified as noncombustible building materials in accordance with ASTM E136.
- ResCom® Board product is a lightweight and integrated insulating, cladding, and finishing system for new construction and remodeling of residential and commercial projects.
The following technical information & test results are the Exclusive Property & Ownership of RGBP Global Group of Companies www.rescombp.com. All results are that of ResCom® (CMC) ISO 8336 certified, patented & manufactured products by ResCom® Building Products. Test results are not transferable to ANY, THIRD PARTY company or product.
If in doubt, contact: rescombp@rescombp.com
RESCOM® CMC ISO:8336 COMPLIANCE TEST REGISTER
| Physical Properties | Testing Standard | Performance | Condition |
|---|---|---|---|
| Reaction to fire: 10mm W&C Lining | AS ISO 9239.1-2003 Part 1 | 0/0/0/0 | HF-30(kW/m2) |
| Reaction to fire: 20mm SF | AS ISO 9239.1-2003 Part 1 | 0/0/0/0 | HF-30(kW/m2) |
| Flame Spread & Combustibility | AS/NZS; 1530.1: 2014 | Class A | As per test standards |
| Flame Spread & Combustibility | AS/NZS 3837:1998 | Class A | As per test standards |
| Flame Spread & Combustibility | ASTM E84 | Class A | As per test standards |
| Flame Spread & Combustibility | ASTM E276B-11 | Class A | As per test standards |
| Flame Spread & Combustibility | BS 476: Part 4 | Class One | As per test standards |
| Flame Spread & Combustibility | BS 476: Part 5 | Class One | As per test standards |
| Flame Spread & Combustibility | BS 476: Part 6 | Class One | As per test standards |
| Flame Spread & Combustibility | BS 476: Part 7 | Class One | As per test standards |
| Flame Spread & Combustibility | BS 476: Part 11 | Class One | As per test standards |
| Flame Spread & Combustibility | ISO 5660-1:2002 | Class A1 & Afl | As per test standards |
| Flame Spread & Combustibility | EN ISO 1182-210 | Class A1 & Afl | As per test standards |
| Determination to heat combustion | EN ISO 1716-2010 | Class A1 & Afl | As per test standards |
| Non Combustibility | ISO 13501-1:2007+A1:20029 | Class A1 | As per test standards |
| Non Combustibility | ISO 13501-1:2007+A1:20029 | Class Afl | As per test standards |
| FRL Systems Performance | BS 476: Part 21: 1987 | 102/102/71 | As per test standards |
| FRL Systems Performance | BS 476: Part 22 | >30min to <240min | As per test standards |
| FRL Systems Performance | ASTM E119 | >30min to <240min | As per test standards |
| FRL Systems Performance | AS/NZS 1530: Part 4: 2014 | >30min to <240min | As per test standards |
| FRL Systems Performance | AS/NZS:5113 | Pass | As per test standards |
| Thermal Resistance m2.K/W | 0.027 & 0.045 | ASTM C518-10 | As per test standards |
| Thermal Conductivity W/mk | 0.44 | ASTM C518-10 | As per test standards |
| Calorific Value | UNE-EN ISO1716 & 1182:2011 | 0.1092 to 0.2554 | As per test standards |
| Water Impermeability Category A | EN 12467:2012 | Pass | As per test standards |
| Vapour Permeability Category D | EN 12467:2012 Sec 5.4.6 & 7.3.4 | u=80 | As per test standards |
| Freeze-Thaw Category A | EN 12467:2012 Sec 5.5.2 & 7.4.1 | Pass | As per test standards |
| Heat Rain Category A | EN 12467:2012 Sec 5.5.3 & 7.4.2 | Pass | As per test standards |
| Soak-Dry Category A | EN 12467:2012 Sec 5.5.5 & 7.3.6 | Pass | As per test standards |
| Swelling & Thickness | EN 317:1993 | <0.2% | Wet |
| TVOC, Formaldehyde | ISO 16000-3, 6,9 & 11: 2006 & 2011 | Zero | As per test standards |
| Dimensional conformance | ASTM C1185-08 (2012) | Pass | As per test standards |
| Density in kg/m3 | ASTM C1185-08 (2012) | 1000 | As per test standards |
| Water tightness | ASTM C1185-08 (2012) | Pass | As per test standards |
| Water absorption | ASTM C1185-08 (2012) | <13.2% | As per test standards |
| EQ Moisture content | ASTM C1185-08 (2012) | <5% | As per test standards |
| “Moisture movement 30-90% relative humidity *” | ASTM C1185-08 (2012) | 0.064 | As per test standards |
| “Humidified deflection [mm] 32c,40%RH, 48hrs *” | ASTM C1185-08 (2012) | 2.18 | As per test standards |
| Average Bending Strength FL | ASTM C1185-08 (2012) | >14Mpa | Wet |
| Average Bending Strength Wall | EN 12467:2012 Sec 5.4.4 & 7.3.2 | >12Mpa | Wet |
| Transverse Load-Roof: 10, 12, 16mm | ASTM E72-22 Section 12 & 20 | Pass | Test load 4.45kN |
| Concentrated load-Roof 10, 12, 16mm | ASTM E72-22 Section 13 & 21 | Pass | Test load 4.45kN |
| Transverse Load-Roof: 20mm SF | ASTM E72-22 Section 12 & 20 | Pass | Test load 4.45kN |
| Concentrated load-Roof: 20mm SF | ASTM E72-22 Section 13 & 21 | Pass | Test load 4.45kN |